MIL-DTL-3607C
3.2.8.2 Aluminum - A. Pure dense electrodeposited aluminum plating in accordance with MIL-DTL-
83488. Color shall be non-reflective.
3.2.8.3 Zinc-nickel Z. Zinc-nickel alloy plating in accordance with ASTM B841. Color shall be black,
non-reflective.
3.2.8.4 Nickel fluorocarbon polymer (Teflon nickel) N. Nickel with fluorocarbon polymer additives over a
suitable underplate. Color shall be non-reflective.
3.2.8.5 Silver S. Silver plating shall conform to ASTM-B700.
3.2.8.6 Tin T. Tin plating shall conform ASTM-B339 or ASTM-B545.
3.2.9 Rubber sheet. Shall conform to MIL-PRF-15624.
3.2.10 Silicone rubber. Silicone rubber shall conform to class Iia, grade 50 or 60, of A-A-59588, except
that the oil immersion test is not applicable.
3.2.11 Silver solder. Silver solder shall conform to class 1 of QQ-B-654.
3.2.11.1 Flux. Flux used while silver soldering shall conform to O-F-499.
3.2.11.2 Soft solder. Soft solder shall conform to composition Sn60 of J-STD-004, J-STD-005 and J-
STD-006.
3.2.11.3 Recycled, recovered, or environmentally preferable materials. Recycled, recovered, or
environmentally preferable materials should be used to the maximum extent possible, provided that the
material meets or exceeds the operational and maintenance requirements, and promotes economically
advantageous life cycle costs.
3.3 Design and construction. Connectors shall be of the design, construction, and physical dimensions
specified (see 3.1). Wherever feasible, parts having similar electrical characteristics may be combined
(fabricated as a single piece) to simplify construction. Parts of unlike materials may be combined such as
brass and copper beryllium, provided copper beryllium is used in the fabrication of the single-piece
construction.
3.3.1 Metal parts. Unless otherwise specified (see 3.1), all metal parts shall have a silver plating of not
less than 0.0002 inch thick, of sufficient smoothness and density to withstand the salt-spray (corrosion)
test specified in 4.6.4. All other types of plating shall be as specified. (see 3.1). Dimensions of metal
parts shall include the plating (see 3.1).
3.3.2 Screw threads. Screw threads shall conform to FED-STD-H28, and shall have the specified fit after
plating (see 3.1).
3.3.3 Gage tests for contacts of rubber-insert type.
3.3.4 Center contacts (female). The center contacts shall meet the gage tests specified in 4.6.1.1 as
piece parts and 4.6.1.2 in the assembled connector.
3.3.4.1 Outer contacts. The outer contacts shall meet the gage tests specified in 4.6.1.2.2 in the
assembled connector.
3.3.4.1.1 Outer contact solder joint. When outer contacts are tested as specified in 4.6.1.3, there shall be
no signs of loosening.